What is the Powder Coating for aluminium profiles?

Powder coating is a dry surface treatment procedure. After the fine pigment particles are electrostatically treated, they are sprayed on the product to form a coating, which is solidified by a curing oven to form a solid coating. Nowadays, most of the coloured aluminium profiles on the market are achieved by powder coating. The coating thickness can reach 40~120 μm.

什么是鋁型材粉末噴涂？

粉末噴涂是一種干燥的表面處理程序。將細顏料顆粒靜電處理后，將它們噴在產(chǎn)物上以形成涂層，該涂層被固化的烤箱固化以形成固體涂層。

如今，市場上的大多數(shù)彩色的鋁型材都是通過粉末涂料來實現(xiàn)的。涂層厚度可以達到40?120μm。

What are the advantages of Powder Coating for aluminium profiles?

1) The surface is beautiful, durable, scratch-resistant, chemically resistant to attack, and UV-resistant;

2) Environmental protection, no waste liquid discharge;

3) Perfect corner coverage;

4) Uniform colour and wide range of spray colours;

5) The thickness is easy to control and thus is widely used.

鋁型材粉末噴涂的優(yōu)勢：

1、表面美觀、耐用、耐刮擦、耐化學侵蝕、耐紫外線；

2、環(huán)保，無廢液排放；

3、完美角落覆蓋；

4、顏色均勻，噴涂顏色范圍廣泛；

5、厚度易于控制，因此被廣泛應用。

外網(wǎng)資料拓展：

粉末涂料和涂層始于20世紀30年代。最初采用的是將聚乙烯粉末通過火焰噴涂的方式涂在金屬表面上，這是粉末涂料的開始。直到20世紀50年代，在德國發(fā)明了發(fā)明性的粉末床涂覆工藝后，粉末涂料和涂層工藝得到了極大的發(fā)展。

而中國開始比較晚。1989年，江蘇常州華藝鋁型材廠引進了美國 Nordson 粉末涂裝設備，這是中國第一家鋁粉末涂裝。隨著經(jīng)濟改革和開放，粉末涂料技術在中國得到了大力發(fā)展。初期采用的是橫向生產(chǎn)線。但隨著經(jīng)濟技術的發(fā)展，意大利和日本率先引進立式噴涂生產(chǎn)線并開始廣泛應用。立式粉末涂層生產(chǎn)線已經(jīng)發(fā)展成為成熟的產(chǎn)品，從預處理、干燥到粉末涂層的均勻性，再到固化效果，均已達到國外先進水平，由于立式線的占地面積小，操作人員數(shù)量少，噴涂的均勻性和固化層的效果均達到完美的結果。

操作流程

粉末噴涂工藝步驟：上架——酸洗——水洗——鉻化——水洗——烘干——下架——上架——噴涂——固化——成品包裝

水洗：指對鋁型材進行預處理前，先洗去附著于型材表面的雜質油脂等，同時在表面形成水膜，避免與氧氣接觸；

鉻化：鉻酸鹽處理，行業(yè)內(nèi)稱“鉻化”，該工藝影響后續(xù)型材表面附著力和耐腐蝕力；烘干：避免后續(xù)漆膜出現(xiàn)氣泡、脫落等現(xiàn)象固化：粉末融化后，自流平形成永久性膜。